Technical Data
Menu
  • Home
  • About
  • Wire
    • Beryllium Copper Wire
      • Heat Treatable, Alloy 25 (C17200 and C17300)
      • Heat Treatable (C17410)
      • Tempered, Alloy 25 (C17200)
    • Nickel Wire
      • 80-20 Copper-Nickel C71000
      • COPPER-NICKEL-TIN C72500
      • Nickel 205 Grade A
    • Phosphor Bronze Wire
      • Phosphor Bronze, C51000 Grade A
      • Phosphor Bronze C52100 Grade C
      • Phosphor Bronze, C50700 Grade E
    • Brass Wire
      • 70-30 Brass, C26000
    • Copper Wire
      • Copper, Oxygen Free High Conductivity C10200
      • Copper, C11000, ETP
      • Zirconium Copper Wire
    • Copper Alloy Wire
      • C 18080 K-88 Alloy
      • C 18150 Copper Chromium Zirconium (ZCC)
  • Plating
  • Straight And Cut
  • Request Quote
  • Sales Terms
  • Contact
  • Chinese Catalog
CLOSE

Nickel 205 Grade A

Home Nickel Wire Nickel 205 Grade A

NICKEL, 205 Grade A

COMPOSITION
NICKEL, 205 Grade A

ELEMENT PERCENT
MINIMUM MAXIMUM
Nickel plus Cobalt 99.0 –
Copper – .15
Iron – .20
Manganese – .35
Carbon – .15
Magnesium .01 .08
Titanium .01 .05
Silicon – .15
Sulfur – .008

 

PHYSICAL PROPERTIES
NICKEL, 205 Grade A

HEAT TREATED CONDITION ENGLISH UNITS METRIC UNITS
Melting Range 2615-2635°F 1435-1445°C
Density .321 lb/cu in. @ 68°F 8.89 gm/cm@ 20°C
Specific Gravity 8.89 8.89
Coefficient of Thermal Expansion .000079 per °F (68-392°F) .0000146 per °C (20-200°C)
Thermal Conductivity 35 BTU/sq ft/ft/hr/°F @ 68°F .145 cal/sq cm/cm/sec/°C @ 20°C
Electrical Resistivity 57.0 Ohms circ mil per ft @ 68°F 9.5 microhm – cm @ 20°C
Electrical Conductivity 18.2% Copper IACS @ 68°F .105 megohm cm @ 20°C
Specific Heat .109 BTU/lb/°F @ 68°F .109 cal/gm/°C @ 20°C
Modulus of Elasticity (tension) 30,000 KSI 21,000 kg/sq mm
Modulus of Rigidity (torsion) 11,000 KSI 7700 kg/sq mm
Annealing Temperature 1300-1700°F 705-925°C

1 KSI equals 1,000 PSI

MECHANICAL PROPERTIES
NICKEL, 205 Grade A

For Round, Half Round and Square Wire
TEMPER TENSILE STRENGTH YIELD STRENGTH .2% Offset
KSI* nominal MPa** nominal KSI* nominal MPa** nominal
Annealed (A) 55-85 379-586 15-50 103-344
Eighth Hard (1/8H) 80-95 551-655 – –
Quarter Hard (1/4H) 70-95 482-655 – –
Half Hard to Hard 105-140 723-965 105-135 723-930
Spring 125-145 861-1000 105-135 723-930

 

MECHANICAL PROPERTIES
NICKEL, 205 Grade A

For Rolled Flat Wire other than Square

TEMPER

TENSILE STRENGTH

YIELD .2% OFFSET STRENGTH

% ELONGATION in 2″ – in 50mm

KSI* MPa** KSI* MPa**
Annealed 55-75 379-517 15-30 103-206 40-55
Spring 90-130 620-896 70-115 482-792 2-15

NICKEL, 205 Grade A

  • Copyright © Little Falls Alloys
  • 171-191 Caldwell Avenue
    Paterson NJ 07501
  • Tel: (973) 278-1666
    Fax: (973) 278-7345
    Toll Free: (888) LFA-Wire
    (888) 532-9473
  • Email:lfawire@aol.com
Beryllium Copper Wire | Phosphor Bronze Wire | Nickel Wire | Brass Wire | Copper Wire | Zirconium Copper Wire | Zirconium Chromium Wire | Site Map | Wire Blog
Little Falls Alloys, Inc. is committed to offer top quality straighten and cut wire, plated wire and beryllium copper, Contact Us.