Technical Data
Menu
  • Home
  • About
  • Wire
    • Beryllium Copper Wire
      • Heat Treatable, Alloy 25 (C17200 and C17300)
      • Heat Treatable (C17410)
      • Tempered, Alloy 25 (C17200)
    • Nickel Wire
      • 80-20 Copper-Nickel C71000
      • COPPER-NICKEL-TIN C72500
      • Nickel 205 Grade A
    • Phosphor Bronze Wire
      • Phosphor Bronze, C51000 Grade A
      • Phosphor Bronze C52100 Grade C
      • Phosphor Bronze, C50700 Grade E
    • Brass Wire
      • 70-30 Brass, C26000
    • Copper Wire
      • Copper, Oxygen Free High Conductivity C10200
      • Copper, C11000, ETP
      • Zirconium Copper Wire
    • Copper Alloy Wire
      • C 18080 K-88 Alloy
      • C 18150 Copper Chromium Zirconium (ZCC)
  • Plating
  • Straight And Cut
  • Request Quote
  • Sales Terms
  • Contact
  • Chinese Catalog
CLOSE

Phosphor Bronze C52100 Grade C

Home Phosphor Bronze Wire Phosphor Bronze C52100 Grade C

PHOSPHOR BRONZE
C52100 Grade C

COMPOSITION
PHOSPHOR BRONZE C52100 GRADE C

ELEMENT PERCENT
NOMINAL MINIMUM MAXIMUM
Tin 8.0 7.0 9.0
Phosphorus – .03 .35
Iron – – .10
Lead – – .05
Zinc – – .20
Copper & Tin
& Phosphorus
– 99.5 –

 

PHYSICAL PROPERTIES
PHOSPHOR BRONZE C52100 GRADE C

HEAT TREATED CONDITION ENGLISH UNITS METRIC UNITS
Melting Range 1620-1880°F 880-1020°C
Density .318 lb/cu in. @ 68°F 8.80 gm/cm@ 20°C
Specific Gravity 8.80 8.80
Coefficient of Thermal
Expansion
.00000101 per °F (68-392°F) .0000182 per °C (20-200°C)
Thermal Conductivity 36 BTU/sq ft/ft/hr/°F @ 68°F .15 cal/sq cm/cm/sec/°C @ 20°C
Electrical Resistivity (Annealed) 79.8 Ohms circ mil per ft @ 68°F 13.3 microhm – cm @ 20°C
Electrical Conductivity
(Annealed)
13% Copper IACS @ 68°F .0754 megohm cm @ 20°C
Specific Heat .09 BTU/lb/°F @ 68°F .09 cal/gm/°C @ 20°C
Modulus of Elasticity (tension) 16,000 KSI 11,200 kg/sq mm
Modulus of Rigidity (torsion) 6000 KSI 4200 kg/sq mm
Annealing Temperature 900-1250°F 480-675°C
Stress Relief Temperature 300-450°F 150-230°C

* 1 KSI equals 1,000 PSI

MECHANICAL PROPERTIES
PHOSPHOR BRONZE C52100 GRADE C

For Round, Half Round and Square Wire
DESIGNATION TENSILE STRENGTH YIELD STRENGTH .2% Offset
STD FORMER KSI* MPa** KSI* MPa**
O61 Annealed (A) 53-68 365-470 17-32 117-220
HO1 Quarter Hard (1/4H) 74-91 510-625 68-85 468-585
HO2 Half Hard (1/2H) 95-115 655-795 80-105 550-724
HO3 Three Quarters Hard (3/4H) 113-135 780-930 105-130 724-895
HO4 Hard 125-150 860-1035 120-145 830-1000
— Extra Hard (Spring) 140 min. 965 min. 135 min. 930 min.

MECHANICAL PROPERTIES
PHOSPHOR BRONZE C52100 GRADE C

For Rolled Flat Wire other than Square
DESIGNATION TENSILE STRENGTH YIELD STRENGTH .2% Offset
STD FORMER KSI* MPa** KSI* MPa**
061 Annealed (A) 53-67 365-460 18-26 124-179
H02 Half Hard (1/2H) 69-84 475-580 57-80 393-551
H04 Hard (H) 85-100 585-690 70-90 482-620
H06 Extra Hard (XH) 97-112 670-770 82-105 565-723
H08 Spring 105-119 725-820 95-115 655-792
H10 Extra Spring 116-122 800-840 100-118 689-813

PHOSPHOR BRONZE C52100 Grade C

  • Copyright © Little Falls Alloys
  • 171-191 Caldwell Avenue
    Paterson NJ 07501
  • Tel: (973) 278-1666
    Fax: (973) 278-7345
    Toll Free: (888) LFA-Wire
    (888) 532-9473
  • Email:lfawire@aol.com
Beryllium Copper Wire | Phosphor Bronze Wire | Nickel Wire | Brass Wire | Copper Wire | Zirconium Copper Wire | Zirconium Chromium Wire | Site Map | Wire Blog
Little Falls Alloys, Inc. is committed to offer top quality straighten and cut wire, plated wire and beryllium copper, Contact Us.