Technical Data
Menu
  • Home
  • About
  • Wire
    • Beryllium Copper Wire
      • Heat Treatable, Alloy 25 (C17200 and C17300)
      • Heat Treatable (C17410)
      • Tempered, Alloy 25 (C17200)
    • Nickel Wire
      • 80-20 Copper-Nickel C71000
      • COPPER-NICKEL-TIN C72500
      • Nickel 205 Grade A
    • Phosphor Bronze Wire
      • Phosphor Bronze, C51000 Grade A
      • Phosphor Bronze C52100 Grade C
      • Phosphor Bronze, C50700 Grade E
    • Brass Wire
      • 70-30 Brass, C26000
    • Copper Wire
      • Copper, Oxygen Free High Conductivity C10200
      • Copper, C11000, ETP
      • Zirconium Copper Wire
    • Copper Alloy Wire
      • C 18080 K-88 Alloy
      • C 18150 Copper Chromium Zirconium (ZCC)
  • Plating
  • Straight And Cut
  • Request Quote
  • Sales Terms
  • Contact
  • Chinese Catalog
CLOSE

Zirconium Copper Wire

Home Copper Wire Zirconium Copper Wire

ZIRCONIUM COPPER, C15000, AMZIRC

 

COMPOSITION
ZIRCONIUM COPPER, C15000, Amzirc

ELEMENT PERCENT
MINIMUM MAXIMUM
Copper & Silver 99.8% —
Zirconium .10

 

.20

 

 

PHYSICAL PROPERTIES
ZIRCONIUM COPPER, C15000, Amzirc

 

ENGLISH UNITS

 

METRIC UNITS

 

Melting Range

 

1795-1975°F

 

980-1080°C

 

Density

 

.321 lb/cu in. @ 68°F

 

8.89 gm/cm@ 20°C

 

Specific Gravity

 

8.89

 

8.89

 

Coefficient of Thermal Expansion

 

.000094 per °F (68-572°F)

 

.000017 per °C (20-300°C)

 

Thermal Conductivity

 

212 BTU/sq ft/ft/hr/°F @ 68°F

 

.876 cal/sq cm/cm/sec/°C @ 20°C

 

Electrical Resistivity (Aged)

 

11.2 Ohms circ mil per ft @ 68°F

 

1.86 microhm – cm @ 20°C

 

Electrical Conductivity (Aged)†

 

93% Copper IACS @ 68°F

 

.538 megohm cm @ 20°C

 

Specific Heat

 

.092 BTU/lb/°F @ 68°F

 

.092 cal/gm/°C @ 20°C

 

Modulus of Elasticity (tension)

 

18,700 KSI

 

13,000 kg/sq mm

 

Modulus of Rigidity (torsion)

 

7300 KSI

 

5000 kg/sq mm

 

Annealing Temperature ††

 

1600-1700°F

 

870-970°C

Aging Temperature
Annealed
Hard

930-1020°F (1-4 hr.)
700-890°F (1-4 hr.)

500-550°C (1-4 hr.)
370-475°C (1-4 hr.)

 

 

MECHANICAL PROPERTIES
ZIRCONIUM COPPER, C15000, Amzirc

For Round and Square Wire, after aging at 750°F (400°C) for one hour
DESIGNATION TENSILE STRENGTH YIELD STRENGTH
2% OFFSET

 

PERCENT ELONGATION
IN 2 in.
IN 50 mm

KSI* MPa** KSI* MPa**
Annealed (A) 35 241 10 68 55
Half Hard (1/2H) 62 427 53 365 11
Hard (H) 68 468 60 413 10
Extra Hard (XH) 70 482 62 427 10.5
Spring 72 496 63 434 11

 

 

MECHANICAL PROPERTIES
ZIRCONIUM COPPER, C15000, Amzirc

For Flat Wire,
Solution annealed at 1650°F (900°C) for 30 minutes, cold rolled and aged one hour
DESIGNATION TENSILE STRENGTH YIELD STRENGTH
2% OFFSET

 

PERCENT ELONGATION
IN 2 in.
IN 50 mm

 

AGING
TEMP.

KSI* MPa** KSI* MPa**
Half Hard (1/2H) 45 310 38 262 18 795°f
(425°C)
Three Quarters Hard (3/4H) 51 351 43 296 15
Hard (H) 54 372 45 310 15 750°F (400°C)
Extra Hard (XH) 57 393 50 344 12
Spring 60 413 52 358 12 705°F (375°C)

 

 

MECHANICAL PROPERTIES
ZIRCONIUM COPPER, C15000, AmzircŽ

 

Retention of Room Temperature Properties
after 50 hours exposure at high temperature

EXPOSURE TEMPERATURE TENSILE STRENGTH
BEFORE EXPOSURE AFTER EXPOSURE
KSI* MPa** KSI* MPa**
660°F (350°C) 69 475 67 —
750°F (400°C) 67.5 465 62 —

 

 

Endurance Strength Compared with Copper

Zirconium Copper 28 KSI for 100,000,000 Cycles
Pure Copper 17 KSI for 100,000,000 Cycles

* 1 KSI equals 1,000 PSI
** 1 KSI equals 6.894,757 MPa
†† Tensile Strength and Grain Size determining factors for acceptance or rejection.
Values for reference only. Not part of specification.

ZIRCONIUM COPPER, C15000, AMZIRC

 

Related ReadingBeryllium Copper
Beryllium Copper wire, Plated wire, Phosphor Bronze wire – Little Falls Alloys offers a full service approach to the Flat wire and Square wire.

  • Copper Alloys such as Nickel Copper
  • FAQ: Zirconium
  • What is Zirconium Copper?

  • Copyright © Little Falls Alloys
  • 171-191 Caldwell Avenue
    Paterson NJ 07501
  • Tel: (973) 278-1666
    Fax: (973) 278-7345
    Toll Free: (888) LFA-Wire
    (888) 532-9473
  • Email:lfawire@aol.com
Beryllium Copper Wire | Phosphor Bronze Wire | Nickel Wire | Brass Wire | Copper Wire | Zirconium Copper Wire | Zirconium Chromium Wire | Site Map | Wire Blog
Little Falls Alloys, Inc. is committed to offer top quality straighten and cut wire, plated wire and beryllium copper, Contact Us.